Metod för att producera raffinerad kromoxidgrön, pigmentgrön 17, CI 77288

Metod för att producera raffinerad kromoxidgrön, pigmentgrön 17, CI 77288

 

1) Egenskaperna hos kromoxidgrön .

Kromoxidgrön, hexagonal kristallfamilj eller amorft mörkgrönt pulver, med metallisk glans . Det finns vanligtvis två nyanser: lätt olivgrön och djup olivgrön, med en metallisk färg . relativ täthet 5 . 21, smältpunkt 2266 Grad, boiling 4000 examen 4000 examen 4000 examen {{7 {kan ha utmärkt värme. withstand a temperature of 1000℃without discoloration, and has excellent acid and alkali resistance. The product has high purity, small particle size, uniform distribution, and extremely hard crystals. Extremely stable, even when hydrogen gas is introduced under red heat, there is no change. Soluble in heated Potassium bromate solution, slightly soluble in acids and bases, Nästan olöslig i vatten, etanol och aceton.

 

2) Applicering av kromoxidgrön pulver .

Chromium oxide green is mainly used for special steel smelting tapping holes, sliding plate openings, and large incinerators. It can be used for coloring ceramics and enamels, coloring rubber, preparing high-temperature resistant coatings, art pigments, and printing ink for paper currency and securities.

Färgen på kromoxidgrön liknar den för växtklorofyll och kan användas som kamouflagfärg, vilket gör det svårt att skilja i infraröd fotografering .

Det används också allmänt i metallurgi, tillverkning av eldfasta material och slipande pulver .

Det kan också användas som en katalysator för organisk syntes och är ett bra grönt pigment, som används i fält som grönt golv, grönt glas och färgad cement .

3) Kromoxid används som pigment och kallas kromoxidgrön .

Det finns många beredningsprocesser, men det finns främst tre vanligt använda metoder: framställning av kromoxid från kromoxid, den termiska sönderdelningsmetoden för ammoniumsulfat natriumalum och den direkta termiska nedbrytningsmetoden för kromanhydrid .

 

3.1) Ammoniumsulfat ton - natrium alum termisk nedbrytningsmetod

This method is the basic method for producing chromium oxide in countries such as the United States, Britain, and Germany, and has become the production method with the largest output, best quality, and most varieties of chromium oxide in foreign countries. Its advantages are that the production process is simpler than that of the liquid phase reduction method, the cost is lower than that of the chromic anhydride decomposition method, the adaptability is wide (it can produce pigments, abrasives, refractories and metallurgical chromium oxide), it is suitable for large-scale production in Rotary kiln, and basically no harmful gas is produced in the production process. Therefore, it replaces the early thermal decomposition method of sodium alum and ammonium chloride. Almost all commercial chromium oxide is directly or indirectly produced from sodium alun och dess produktion står för cirka 20% av konsumtionen av natriumalum

Den totala produktionskapaciteten för kromoxid i olika länder runt om i världen är cirka 100, 000 ton per år .

 

3 . 2) Direkt termisk nedbrytningsmetod för kromanhydrid.

Chromic anhydride thermal decomposition method: Chromic anhydride is thermally decomposed at 900℃under high temperature conditions, and slightly cooled before being crushed to obtain the finished product. In recent years, the development of chromic oxide produced by this method in China has been very rapid. In 1999, the output of chromic oxide produced by chromic anhydride was about 13000 tons, which is twice as complex as the thermal decomposition process of chromic anhydride of metallurgical grade chromic oxide produced by Sodium chromate reduction in Tietai Gold Plant. As the temperature rises, chromic anhydride will decompose into four kinds of chromium oxides. As the chromic anhydride melts at about 200℃and begins to decompose, oxygen and chromic oxide will be precipitated, so as the temperature rises, Chromium oxide crystals can gradually form and grow in the chromic anhydride melt. This method has less Crystallographic defect, can maintain many excellent properties of chromium oxide single crystal, and has high product quality, so it is widely used. Research has shown that Cr2O3 is already produced when the temperature rises to 470℃, and has been completely converted to Cr2O3 by 550V. However, during the experiment, it was found that the actual decomposition temperature was higher than this temperature. The reason is that during the decomposition process of Cr2O3, a Cr2O3 thin film is generated to coat the surface of the unconverted chromium oxide, while the melting point of Cr2O3 is very high (2266 ± 25)℃, and the poor heat transfer hinders the further decomposition of the chromium oxide. To achieve this, a process of adding a small amount of water can be used to reduce the reaction temperature. On the one hand, Cr2O3 is highly soluble in water, and on the other hand, it can make the additive and Cr2O3 raw material mix jämnt . Provanalysresultaten indikerar att massfraktionen av CR2O3 har nått över 99%. Reaktionstemperaturen och tiden har också en betydande inverkan på nedbrytningen av kromanhydrid .}

 

3.3) Framställning av krom (iii) oxid från kromoxid

Up to now, although there are many methods to produce Chromium(III) hydroxide from Chromium(III) sulfate solution through neutralization and separation, the Chromium(III) hydroxide generated is a fine colloidal substance, which is difficult to treat and has low purity. After long-term storage, it is insoluble in acid and alkali; Dessutom, om neutralisatorn använder alkalimetallhydroxider eller karbonater, kommer den att bilda olöslig eller olöslig biprodukter, vilket begränsar användningen av neutralisatorn och begränsar den här metoden . för att lösa detta problem, tyska patent 418050 föreslog följande reaktionsmetod för att producera CHROMIZ (III) för att lösa detta problem, tyska patent 418050 Förslag till följande reaktionsmetod för att producera CHROMIZ (III) för att lösa detta problem, tyska patent 418050 Förslag till följande reaktionsmetod för att producera CHROMION (III) HYDRODE:

Men denna metod har också defekter: operationen är komplex, och järn är lätt att blanda med krom (iii) hydroxidhandduk . Därför framställs krom (iii) hydroxid genom neutralisering av krom (iii) kloridvattig lösning som är lätt att använda .}}}

Dessutom används det vattenlösliga trivalenta kromsaltet för att producera kromoxid genom krom (III) hydroxid eller kromhydroxid (Crooh); Med användning av krom som innehåller avfall för att producera kromoxid; Beredning av kromoxid av pigmentkvalitet från kromoxid utan pigmentkvalitet; Direkt produktion av smältblåst kromoxid med användning av aluminotermiska eller silikotermiska metoder .

 

Välkommen till förfrågan merKromoxidgrönvia e -post:Vip@Greefield.com eller av whatsapp:+86139 5726 4669smidigt, TDS -begäran igenomWhatsapp .